Refractories subject to loading and unloading repeatedly because of physical effects and thermal stress attack in the service process, which is an important issue shortening the service life of the thermal equipment. Therefore, researches of predicting the service life of refractories under...
Fully dense Al2TiO5–Al2O3–TiN (ATN) composites were fabricated by reactive sintering using spark plasma sintering at 1400°C for 5 min under 100 MPa in vacuum. An equimolar ratio of Al2O3:TiO2 was used as the starting powder, while the addition of 0–36 mol% AlN was investigated. The thermodynamic...
Neodymium-doped phosphates, (Nd1-x Gd x )0.33Zr2(PO4)3 (0 ≤ x ≤ 1), were synthesized by co-precipitation. (Nd1-x Gd x )0.33Zr2(PO4)3 was obtained as a single-phase and was confirmed to be a NASICON-type structure consisting of a three-dimensional network of PO4 tetrahedra sharing corners with...
Read and print from thousands of top scholarly journals.
Continue with Facebook
Sign up with Google
Log in with Microsoft
Already have an account? Log in
Bookmark this article. You can see your Bookmarks on your DeepDyve Library.
To save an article, log in first, or sign up for a DeepDyve account if you don’t already have one.
Sign Up Log In
To subscribe to email alerts, please log in first, or sign up for a DeepDyve account if you don’t already have one.
To get new article updates from a journal on your personalized homepage, please log in first, or sign up for a DeepDyve account if you don’t already have one.