Amalgam buildups: shear strength and dentin sealing properties.

Amalgam buildups: shear strength and dentin sealing properties. The retentive strength and sealing properties of amalgam buildups were compared in vitro in three groups of specimens. All teeth were prepared with flat, nonretentive surfaces. In the first group, the amalgam buildups were retained by four self-threading Minim pins. In the second group, retention was provided by a circumferential slot prepared in the dentin just inside the DEJ. The third group utilized an adhesive resin for retention. Dentin permeability was measured as a hydraulic conductance before and after placement of the amalgam buildups and before and after thermocycling. All methods of retention sealed dentin very well even in the absence of cavity varnish. The 90 degree retentive strength was: pins, 10.3 +/- 0.9 MPa; slots, 4.1 +/- 0.5 MPa; resin, 3.1 +/- 0.8 MPa (mean +/- SEM). http://www.deepdyve.com/assets/images/DeepDyve-Logo-lg.png Operative dentistry Pubmed

Amalgam buildups: shear strength and dentin sealing properties.

Operative dentistry , Volume 16 (3): 8 – Apr 29, 1992

Amalgam buildups: shear strength and dentin sealing properties.


Abstract

The retentive strength and sealing properties of amalgam buildups were compared in vitro in three groups of specimens. All teeth were prepared with flat, nonretentive surfaces. In the first group, the amalgam buildups were retained by four self-threading Minim pins. In the second group, retention was provided by a circumferential slot prepared in the dentin just inside the DEJ. The third group utilized an adhesive resin for retention. Dentin permeability was measured as a hydraulic conductance before and after placement of the amalgam buildups and before and after thermocycling. All methods of retention sealed dentin very well even in the absence of cavity varnish. The 90 degree retentive strength was: pins, 10.3 +/- 0.9 MPa; slots, 4.1 +/- 0.5 MPa; resin, 3.1 +/- 0.8 MPa (mean +/- SEM).

Loading next page...
 
/lp/pubmed/amalgam-buildups-shear-strength-and-dentin-sealing-properties-0x07DOpqkP

References

References for this paper are not available at this time. We will be adding them shortly, thank you for your patience.

ISSN
0361-7734
pmid
1803337

Abstract

The retentive strength and sealing properties of amalgam buildups were compared in vitro in three groups of specimens. All teeth were prepared with flat, nonretentive surfaces. In the first group, the amalgam buildups were retained by four self-threading Minim pins. In the second group, retention was provided by a circumferential slot prepared in the dentin just inside the DEJ. The third group utilized an adhesive resin for retention. Dentin permeability was measured as a hydraulic conductance before and after placement of the amalgam buildups and before and after thermocycling. All methods of retention sealed dentin very well even in the absence of cavity varnish. The 90 degree retentive strength was: pins, 10.3 +/- 0.9 MPa; slots, 4.1 +/- 0.5 MPa; resin, 3.1 +/- 0.8 MPa (mean +/- SEM).